Negative electrode active material for lithium ion secondary battery, negative electrode for lithium ion secondary battery, and lithium ion secondary battery

ABSTRACT

A negative electrode active material for a lithium ion secondary battery, the negative electrode active material includes silicon oxide particles, each of which has carbon on at least a portion of its surface, in which: a ratio (P Si /P SiO2 ) of an intensity of an X-ray diffraction peak at 2θ of from 27° to 29°, which is derived from Si, to an intensity of an X-ray diffraction peak at 2θ of from 20° to 25°, which is derived from SiO 2 , is within a range of from 1.0 to 2.6, when CuKα radiation having a wavelength of 0.15406 nm is used as a radiation source; and a specific surface area calculated from moisture adsorption at 298 K is 6.5 m 2 /g or less.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a U.S. national phase application filed under 35U.S.C. § 371 of International Application No. PCT/JP2018/003284, filedJan. 31, 2018, designating the United States, the entire contents ofwhich are hereby incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to a negative electrode active materialfor a lithium ion secondary battery, a negative electrode for a lithiumion secondary battery, and a lithium ion secondary battery.

BACKGROUND ART

Graphite has been mainly used currently as a negative electrode activematerial for a lithium ion secondary battery. It is known that graphitehas a theoretical maximum discharge capacity of 372 mAh/g. In recentyears, in association with an increase in the performance of mobiledevices, such as cell phones, notebook computers, and tablet-typeterminals, demand for development of a negative electrode activematerial capable of further improving capacity of a lithium ionsecondary battery exists.

Having as a background the condition set forth above, it has beenstudied for using, as a negative electrode active material, materialshaving higher theoretical capacity than graphite. Among such compounds,silicon oxides, which have a higher capacity, which are inexpensive, andwhich have excellent processability, are thus particularly intensivelyresearched in terms of applications as negative electrode activematerials.

For example, Patent Literature 1 discloses a negative electrode activematerial, characterized in that a particle having a structure in whichmicrocrystals of silicon are dispersed in a silicon compound is coatedon the surface thereof with carbon, in which a diffraction peak derivedfrom Si (111) is observed in x-ray diffractometry, and the siliconcrystallite has a size of from 1 nm to 500 nm determined by a Scherrermethod based on a half-value width of the diffraction peak.

According to the technique described in Patent Literature 1, it isregarded that, by dispersing microcrystals or microparticles of siliconin an inert robust substance such as, for example, silicon dioxide, andfurther fusing carbon to at least a part of the surface thereof forimparting conductivity, a structure that not only has stable surfaceconductivity but is also stable against volume changes of siliconassociated with absorption and desorption of lithium can be obtained, asa result of which long-term stability and initial efficiency can beimproved.

Patent Literature 2 discloses a negative electrode active material,characterized in that a surface of a silicon oxide particle is coatedwith a graphite film, in which the amount of graphite coating is from 3%by weight to 40% by weight, a BET specific surface area is from 2 m²/gto 30 m²/g, and the graphite film has a graphite structure-intrinsicspectrum with Raman shifts of near 1330 cm⁻¹ and near 1580 cm⁻¹ by Ramanspectroscopy.

According to the technique described in Patent Literature 2, it isregarded that, by adjusting the physical property of the graphite filmfor coating the surface of the material capable of absorbing anddesorbing a lithium ion to a specific range, a negative electrode for alithium ion secondary battery that may achieve a property levelsatisfying demands of the market can be obtained.

Patent Literature 3 discloses a negative electrode active material, inwhich a surface of a particle of a silicon oxide represented by aformula SiO_(x) is coated with a carbon film and the carbon film is athermal plasma treated film.

According to the technique described in Patent Literature 3, it isregarded that a negative electrode active material with which theproblems of expansion of the electrode, which is a drawback of a siliconoxide, and expansion of the battery due to gas generation can be solved,and which has excellent cycle characteristics can be obtained.

RELATED ART DOCUMENT Patent Document

Patent Literature 1: Japanese Patent No. 3952180

Patent Literature 2: Japanese Patent No. 4171897

Patent Literature 3: Japanese Patent Application Laid-Open (JP-A) No.2011-90869

In future, it will be required that a negative electrode active materialto be applied to a lithium ion secondary battery suitable for improvingthe performance of mobile devices and the like can store a large amountof lithium ions (that is, required to have a higher capacity) as well asto desorb more lithium ions that have been stored therein. Therefore,with regard to a negative electrode active material that contributes tofurther improvement in the performance of a lithium ion secondarybattery, improvements in the initial discharge capacity is important. Inaddition, high temperature storage characteristics of lithium-ionbatteries, using the recovery rate after charging and discharging as anindicator, need to be further improved.

An embodiment of the present invention is made in consideration of theabove demands, and an object of the invention is to provide a negativeelectrode active material for a lithium ion secondary battery which mayimprove an initial discharge capacity and a storage characteristics athigh temperature of a lithium ion secondary battery, a negativeelectrode for a lithium ion secondary battery using the same, and alithium ion secondary battery using the same.

Solution to Problem

The specific means to solve the problems are as follows.

<1> A negative electrode active material for a lithium ion secondarybattery, the negative electrode active material including silicon oxideparticles, each of which has carbon on at least a portion of itssurface, in which:

a ratio (P_(Si)/P_(SiO2)) of an intensity of an X-ray diffraction peakat 2θ of from 27° to 29°, which is derived from Si, to an intensity ofan X-ray diffraction peak at 2θ of from 20° to 25°, which is derivedfrom SiO₂, is within a range of from 1.0 to 2.6, when CuKα radiationhaving a wavelength of 0.15406 nm is used as a radiation source; and

a specific surface area calculated from moisture adsorption at 298 K is6.5 m²/g or less.

<2> A negative electrode active material for a lithium ion secondarybattery, the negative electrode active material including silicon oxideparticles, each of which has carbon on at least a portion of itssurface, in which:

a ratio (P_(Si)/P_(SiO2)) of an intensity of an X-ray diffraction peakat 2θ of from 27° to 29°, which is derived from Si, to an intensity ofan X-ray diffraction peak at 2θ of from 20° to 25°, which is derivedfrom SiO₂, is within a range of from 1.0 to 2.6, when CuKα radiationhaving a wavelength of 0.15406 nm is used as a radiation source; and

an amount of adsorption of moisture up to a relative pressure of 0.95 at298 K is 8.5 cm³/g or less.

<3> The negative electrode active material for a lithium ion secondarybattery according to <1> or <2>, in which an mean aspect ratiorepresented by a ratio (S/L) of a minor axis S to a major axis L iswithin a range of 0.45≤S/L≤1.

<4> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <3>, in which the negativeelectrode active material has a ratio (D10%/D90%) of 0.1 or greater, inwhich D90% is a particle diameter corresponding to 90% cumulative from asmaller particle diameter side in a cumulative volume distribution curveobtained by a laser diffraction/scattering method, and D10% is aparticle diameter corresponding to 10% cumulative from the smallerparticle diameter side in the cumulative volume distribution curve.

<5> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <4>, in which a content of thecarbon is within a range from 0.1% by mass to 10.0% by mass of a totalof the silicon oxide particles and the carbon.

<6> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <5>, the negative electrodeactive material having a diffraction peak that is attributed to Si (111)in X-ray diffraction spectra, in which a size of silicon crystallitescalculated from the diffraction peak is from 1.0 nm to 15.0 nm.

<7> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <6>, in which a volume meanparticle diameter is from 0.1 μm to 20 μm.

<8> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <7>, in which a specific surfacearea calculated from nitrogen adsorption at 77 K is from 0.1 m²/g to 10m²/g.

<9> The negative electrode active material for a lithium ion secondarybattery according to any one of <1> to <8>, further including acarbon-based negative electrode active material.

<10> A negative electrode for a lithium ion secondary battery, thenegative electrode including:

a current collector; and

a negative electrode material layer that is provided on or above thecurrent collector and that includes the negative electrode activematerial for a lithium ion secondary battery according to any one of <1>to <9>.

<11> A lithium ion secondary battery, including:

a positive electrode;

the negative electrode for a lithium ion secondary battery according to<10>; and

an electrolyte.

Effects of Invention

According to an embodiment in the invention, there can be provided anegative electrode active material for a lithium ion secondary batterywhich may improve an initial discharge capacity and a storagecharacteristics at high temperature of a lithium ion secondary battery,a negative electrode for a lithium ion secondary battery using the same,and a lithium ion secondary battery using the same.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic sectional view illustrating an example of astructure of a negative electrode active material.

FIG. 2 is a schematic sectional view illustrating another example of astructure of a negative electrode active material.

FIG. 3 is a schematic sectional view illustrating another example of astructure of a negative electrode active material.

FIG. 4 is a schematic sectional view illustrating another example of astructure of a negative electrode active material.

FIG. 5 is a schematic sectional view illustrating another example of astructure of a negative electrode active material.

FIG. 6A is an enlarged schematic sectional view of a portion of thenegative electrode active material shown in FIGS. 1 to 3, illustratingan aspect of the state of carbon 10 in the negative electrode activematerial.

FIG. 6B is an enlarged schematic sectional view of a portion of thenegative electrode active material shown in FIGS. 1 to 3, illustratinganother aspect of the state of carbon 10 in the negative electrodeactive material.

DESCRIPTION OF EMBODIMENTS

Embodiments of the invention are described below in detail. It is notedhere, however, that the invention is not restricted to the embodimentsdescribed below. In the below-described embodiments, the constituentsthereof (including element steps and the like) are not indispensableunless otherwise specified. The same applies to the numerical values andranges thereof, without restricting the invention.

In the present disclosure, the term “process” encompasses not onlyprocesses discrete from other processes but also steps which cannot beclearly distinguished from other processes, as long as the intendedpurpose of the process is achieved.

In the present disclosure, each numerical range specified using “(from). . . to . . . ” represents a range including the numerical values notedbefore and after “to” as the minimum value and the maximum value,respectively.

In a set of numerical ranges that are stated stepwisely in the presentspecification, the upper limit value or the lower limit value of anumerical range may be replaced with the upper limit value or the lowerlimit value of other numerical range. Further, in a numerical rangestated in the present specification, the upper limit value or the lowerlimit value of the numerical range may be replaced with a relevant valueindicated in any of Examples.

In the present disclosure, each component may include plural kinds ofsubstances corresponding to the component. In a case in which there areplural kinds of substances that correspond to a component of acomposition, the indicated content ratio or amount of the component inthe composition means, unless otherwise specified, a total content ratioor amount of the plural kinds of substances existing in the composition.

In the present disclosure, each component may include plural kinds ofparticles corresponding to the component. In a case in which there areplural kinds of particles that correspond to a component of acomposition, the indicated particle diameter of the component in thecomposition means, unless otherwise specified, a value determined for amixture of the plural kinds of particles existing in the composition.

In the present disclosure, the term “layer” or “film” includes, whenobserving a region where the layer or the film is present, a case inwhich the layer or the film is formed only on a part of the region inaddition to a case in which the layer or the film is formed on theentirety of the region.

In the present disclosure, the term “layered” as used herein indicatesthat plural layers are piled up, in which two or more layers may bebonded to each other or may be detachable from each other.

In the present disclosure, when embodiments are explained with referringto any Figure, the embodiments are not restricted to the configurationshown in the Figure. Sizes of members shown in each of the Figures areconceptual, and relative relationship in size of the members is notrestricted to that shown therein.

<Negative Electrode Active Material for Lithium Ion Secondary Battery(First Embodiment)>

The negative electrode active material for a lithium ion secondarybattery in the present disclosure (hereinafter, also abbreviated simplyto “negative electrode active material”) includes silicon oxideparticles, each of which has carbon on at least a portion of itssurface, wherein: a ratio (P_(Si)/P_(SiO2)) of an intensity of an X-raydiffraction peak at 2θ of from 27° to 29°, which is derived from Si, toan intensity of an X-ray diffraction peak at 2θ of from 20° to 25°,which is derived from SiO₂, is within a range of from 1.0 to 2.6, whenCuKα radiation having a wavelength of 0.15406 nm is used as a radiationsource; and a specific surface area calculated from moisture adsorptionat 298 K is 6.5 m²/g or less.

(Silicon Oxide Particle)

The silicon oxide which forms the silicon oxide particles included inthe negative electrode active material may be any one as long as it isan oxide containing a silicon element, and examples thereof includeoxidized silicon, silicon dioxide, and silicon suboxide. The siliconoxide included in the silicon oxide particles may be only one kind or acombination of two or more kinds thereof.

Among the silicon oxides, oxidized silicon and silicon dioxide aregenerally represented by silicon monoxide (SiO) and silicon dioxide(SiO₂), respectively. However, depending on the surface state (forexample, presence of an oxide film) or the condition of compositiongeneration, the silicon oxide is sometimes represented by thecomposition formula SiO_(x) (x represents 0<x≤2) as an actual measuredvalue (or a corresponding value) of an element contained, and this caseis also included in the silicon oxide according to the presentdisclosure. Here, the value of x in the composition formula can becalculated by measuring oxygen contained in the silicon oxide by aninert gas fusion-nondispersive infrared absorption method. In a case inwhich a disproportionation reaction (2SiO→Si+SiO₂) of the silicon oxideis associated with the manufacturing process of the negative electrodeactive material, the silicon oxide is sometimes represented by the stateincluding silicon and silicon dioxide (or in some cases, oxidizedsilicon) in the chemical reaction, and this case is also included in thesilicon oxide according to the present disclosure.

A mean particle diameter of the silicon oxide particles is notparticularly limited. For example, a volume mean particle diameterthereof is preferably from 0.1 μm to 20 μm, and more preferably from 0.5μm to 10 μm, according to a desired final size of the negative electrodematerial. The volume mean particle diameter of the silicon oxideparticles is D50% which is a particle diameter corresponding to 50%cumulative from the smaller particle diameter side in a volume-basedparticle size distribution curve. The same applies to an expression of amean particle diameter described below. The volume mean particlediameter is measured by a laser diffraction/scattering method by themethod described in Examples below.

(Carbon)

Carbon is present on a part or an entire of the surface of each of thesilicon oxide particles. The presence of carbon on a part or an entireof the surface of each of the silicon oxide particle impartsconductivity to the silicon oxide particle, which is an insulator, andimproves the efficiency of the charge-discharge reaction. It isconsidered that the initial discharge capacity and the initialcharge/discharge efficiency are thus improved. Hereinafter, the siliconoxide particle in which carbon is present on a part or an entire of thesurface is sometimes referred to as a “SiO—C particle”.

In the present disclosure, examples of the carbon present on a part oran entire of the surface of the silicon oxide particle include graphite,amorphous carbon, and the like. It is noted that an organic substancedescribed below does not fall under the “carbon” in the presentdisclosure.

The manner in which the carbon is present on a part or an entire of thesurface of the silicon oxide particle is not particularly limited. Forexample, continuous or discontinuous coating and the like can bementioned.

The presence or absence of carbon in the negative electrode activematerial for a lithium ion secondary battery can be observed by, forexample, laser Raman spectroscopy at an excitation wavelength of 532 nmor the like.

A content of the carbon is preferably from 0.1% by mass to 10.0% by massin a total content of a mass of the silicon oxide particles and a massof the carbon. With such a configuration, the initial discharge capacityand the initial charge/discharge efficiency tend to be further improved.The content of the carbon is more preferably from 1.0% by mass to 9.0%by mass, more preferably from 2.0% by mass to 8.0% by mass, andparticularly preferably from 3.0% by mass to 7.0% by mass.

A content (in terms of mass) of the carbon can be determined by, forexample, a high-frequency furnace combustion-infrared absorptionspectrometry. For example, in the high-frequency furnacecombustion-infrared absorption spectrometry, a sulfur/carbonsimultaneous analyzer (CSLS600, manufactured by LECO Japan Corporation)may be used. In a case in which the negative electrode active materialcontains the organic substance described below, the content ratio of thecarbon can be measured by removing from the negative electrode activematerial, in advance, a to-be-decreased mass derived from the organicsubstance by heating the negative electrode active material to atemperature which is higher than a temperature at which the organicsubstance degrades (for example, at 300° C.).

The carbon is preferably a carbon with low crystallinity. In the presentdisclosure, the expression that the carbon is with “low crystallinity”means that an R value of a negative electrode active material obtainedby the following method is 0.5 or more.

The R value of a negative electrode active material means a peakintensity ratio Id/Ig (also referred to as D/G), in which Id is a peakintensity at around 1360 cm⁻¹ and Ig is a peak intensity at around 1580cm⁻¹, in a profile of a laser Raman spectrum measurement with awavelength of 532 nm.

Here, the peak at around 1360 cm⁻¹ is a peak that is generallyidentified as corresponding to an amorphous structure, and for exampleit is a peak observed at from 1300 cm⁻¹ to 1400 cm⁻¹. The peak at around1580 cm⁻¹ is a peak that generally identified as corresponding to thegraphite crystal structure, and for example it is a peak observed atfrom 1530 cm⁻¹ to 1630 cm⁻¹.

The R value can be determined using a Raman spectrum measuring apparatus(for example, NSR 1000 manufactured by JASCO Corporation) with setting abaseline to 1050 cm⁻¹ to 1750 cm⁻¹ with respect to a measurement range(from 830 cm⁻¹ to 1940 cm⁻¹).

The R value of the negative electrode active material is preferably from0.5 to 1.5, more preferably from 0.7 to 1.3, and still more preferablyfrom 0.8 to 1.2. In a case in which the R value is from 0.5 to 1.5, asurface of the silicon oxide particle is sufficiently covered withlow-crystallinity carbon in which carbon crystallites are randomlyoriented, so that a reactivity with an electrolyte solution can bereduced and the cycle characteristics tend to be improved.

A method of applying carbon to a surface of the silicon oxide particleis not particularly limited. Specific examples thereof include a wetmixing method, a dry mixing method, a chemical vapor deposition methodand the like.

In a case in which the application of carbon is performed by way of thewet mixing method, examples thereof include a method which includesmixing the silicon oxide particles with a substance in which a rawmaterial of carbon (a carbon source) is dissolved or dispersed in asolvent, attaching the carbon source to the surfaces of the siliconoxide particles, removing the solvent if needed, and then subjecting theresultant to a heat treatment in an inert atmosphere to carbonize thecarbon source.

In a case in which the application of carbon is performed by way of thedry mixing method, examples thereof include a method in which a mixtureis prepared by mixing the silicon oxide particles in a solid state andthe carbon source in a solid state, and the mixture is subjected to aheat treatment in an inert atmosphere to carbonize the carbon source. Atreatment for imparting mechanical energy (such as a mechanochemicaltreatment) may be performed when mixing the silicon oxide particles withthe carbon source.

In a case in which the application of carbon is performed by way of thechemical vapor deposition method, a known method may be used. Forexample, the silicon oxide particles are subjected to a heat treatmentin an atmosphere containing vaporized gas of the carbon source tocarbonize the carbon source, thereby applying carbon to the surfaces ofthe silicon oxide particles.

In a case in which carbon is applied to the surfaces of the siliconoxide particles by the wet mixing method or the dry mixing method, thecarbon source to be used is not particularly limited as long as it is amaterial which can be changed to carbon by the heat treatment. Specificexamples thereof include polymer compounds such as a phenol resin, astyrene resin, polyvinyl alcohol, polyvinyl chloride, polyvinyl acetate,or polybutyral; pitch such as ethylene heavy end pitch, coal pitch,petroleum pitch, coal tar pitch, asphalt decomposition pitch, PVC pitchobtained by pyrolyzing polyvinyl chloride or the like, or naphthalenepitch prepared by polymerizing naphthalene or the like under thepresence of a super-strong acid; and polysaccharides such as starch orcellulose. The carbon source to be used may be only one kind or acombination of two or more kinds thereof.

In a case in which carbon is applied to the surfaces of the siliconoxide particles by the chemical vapor deposition method, the carbonsource to be used may be an aliphatic hydrocarbon, an aromatichydrocarbon, an alicyclic hydrocarbon or the like, and preferably acompound in the form of a gas or a compound which can be easily madeinto a gas. Specific examples thereof include methane, ethane, propane,toluene, benzene, xylene, styrene, naphthalene, cresol, anthracene, andderivatives thereof. The carbon source to be used may be a natural gas.The carbon source to be used may be only one kind or a combination oftwo or more kinds thereof.

The heat treatment temperature for carbonizing the carbon source is notparticularly limited as long as carbonization of the carbon source canbe achieved at the temperature. The heat treatment temperature ispreferably 700° C. or higher, more preferably 800° C. or higher, andstill more preferably higher than 900° C. From the viewpoints ofobtaining a carbon with low crystallinity and producing the siliconcrystallite having a desired size by the disproportionation reactiondescribed below, the heat treatment temperature is preferably 1300° C.or lower, more preferably 1200° C. or lower, and still more preferably1100° C. or lower.

The duration of the heat treatment for carbonizing the carbon source maybe selected according to the kind, amount and the like of the carbonsource to be used. For example, the duration of the heat treatment ispreferably from 1 hour to 10 hours, and more preferably from 2 hours to7 hours.

The heat treatment for carbonizing the carbon source is preferablyperformed in an inert atmosphere such as nitrogen or argon. The heattreatment apparatus is not particularly limited, and examples thereofinclude a heating apparatus applicable to a continuous or batchtreatment. Specifically, it may be selected from a fluidizedbed-furnace, a revolving furnace, a vertical moving bed furnace, atunnel furnace, a batch furnace, a rotary kiln or the like.

In a case in which carbon is imparted to the surface of the siliconoxide particles by chemical vapor deposition using a rotary furnace orrotary kiln, it is preferable to use an apparatus in which the core tubeof a rotary furnace or rotary kiln is arranged horizontally and the coretube is rotated. The chemical vapor deposition treatment of the siliconoxide particles while rotating silicon oxide particles enables stableproduction without aggregation of the silicon oxide particles. Theabove-described apparatus is not limited as long as it has a furnacecore tube capable of holding an atmosphere, a rotation mechanism forrotating the furnace core tube, and a heating mechanism capable ofraising and maintaining the temperature. The above-described apparatusmay be equipped with a raw material feeding mechanism (for example, afeeder) and a product recovery mechanism (for example, a hopper),depending on the purpose, and the furnace core tube may be inclined orequipped with a baffle plate in the furnace core tube in order tocontrol the residence time of the raw material. The material of thefurnace core tube is not particularly restricted, and a ceramic such asalumina or silicon carbide, a high-melting point metal such asmolybdenum or tungsten, SUS, quartz, or the like can be selected asappropriate depending on the processing conditions and the purposes oftreatment.

In a case in which plural particles in the heat-treated product obtainedby the heat treatment form aggregates, a disintegration treatment may befurther performed. In a case in which the adjustment of the meanparticle diameter to an intended size is required, a pulverizationtreatment may further be performed.

(X-Ray Diffraction Peak Intensity Ratio)

The negative electrode active material has an X-ray diffractive peakintensity ratio (P_(Si)/P_(SiO2)) ranging from 1.0 to 2.6. The X-raydiffraction peak intensity ratio (P_(Si)/P_(SiO2)) is a ratio of anintensity of an X-ray diffraction peak at 2θ of from 27° to 29°, whichis derived from Si, to an intensity of an X-ray diffraction peak at 2θof from 20° to 25°, which is derived from SiO₂, when CuKα radiationhaving a wavelength of 0.15406 nm is used as a radiation source.

The ratio (P_(Si)/P_(SiO2)) of the intensities of the X-ray diffractivepeaks of the negative electrode active material may be a value measuredin a state where carbon, the organic substance, a conductive particle,or the like adhere to the silicon oxide particles, or a value measuredin a state where these do not adhere to the silicon oxide particles.

Examples of the negative electrode active material having the ratio ofthe intensities of X-ray diffracted peaks (P_(Si)/P_(SiO2)) ranging from1.0 to 2.6 include a negative electrode active material containing asilicon oxide particle having a structure in which crystallites ofsilicon are present in the silicon oxide.

The silicon oxide particle having a structure in which siliconcrystallites are dispersed in silicon oxide can be produced, forexample, by causing disproportionation reaction of silicon oxide(2SiO→Si+SiO₂) to generate silicon crystallites in the silicon oxideparticle. By controlling the degree of formation of silicon crystallitesin the silicon oxide particle, the ratio of the intensities of the X-raydiffraction peaks can be controlled to a desired value.

An advantage of achieving the presence of silicon crystallites in thesilicon oxide particle by way of the disproportionation reaction ofsilicon oxide can be considered as follows. The above-mentioned SiO_(x)(x is 0<x≤2) tends to be inferior in the initial charge/dischargecharacteristics because lithium ions are trapped at the time of initialcharge. This occurs because lithium ions are trapped by dangling bonds(unshared electron pair) of oxygen present in the amorphous SiO₂ phase.Therefore, it is considered that suppressing generation of danglingbonds of active oxygen atoms by reconstructing the amorphous SiO₂ phaseby heat treatment is preferable from the viewpoint of improvement incharge-discharge characteristics.

In a case in which the ratio (P_(Si)/P_(SiO2)) of the intensities of theX-ray diffraction peaks of the negative electrode active material is 1.0or more, the crystallites of silicon in the silicon oxide particle growsufficiently and the ratio of SiO₂ does not become large, so that adecrease of the cycle characteristics tends to be suppressed. On theother hand, in a case in which the ratio (P_(Si)/P_(SiO2)) is 2.6 orless, the crystallites of the generated silicon are not too large torelieve expansion and contraction, which tends to suppress a decrease inthe initial discharging capacity. From the viewpoint of obtaining anegative electrode active material excellent in charge-dischargecharacteristics, the ratio (P_(Si)/P_(SiO2)) is preferably within therange of from 1.5 to 2.0.

The ratio (P_(Si)/P_(SiO2)) of the intensities of the X-ray diffractedpeaks of the negative electrode active material can be controlled by,for example, the condition of the heat treatment for causing thedisproportionation reaction of the silicon oxide. For example, byincreasing the temperature of the heat treatment or increasing the heattreatment time, the generation and enlargement of silicon crystallitesare promoted, and the ratio of the intensities of the X-ray diffractionpeaks can be increased. On the other hand, by lowering the temperatureof the heat treatment or shortening the heat treatment time, thegeneration of silicon crystallites can be suppressed, and the ratio ofthe intensities of the X-ray diffraction peaks can be reduced.

In a case in which the silicon oxide particle is prepared bydisproportionation reaction of silicon oxide, silicon oxide to be usedas a raw material may be obtained, for example, by a known sublimationtechnique in which a silicon monoxide gas produced by heating a mixtureof silicon dioxide and a metal silicon is cooled and precipitated.Alternatively, it is commercially available as oxidized silicon, siliconmonoxide or the like.

(Size of Silicon Crystallite)

The negative electrode active material preferably has a diffraction peakthat is attributed to Si (111) in the X-ray diffraction spectra, and thesize of silicon crystallites calculated from the diffraction peak ispreferably within a range from 1.0 nm to 15.0 nm. Whether or not siliconcrystallites are present in the silicon oxide particle may be observed,for example, by a powder X-ray diffraction (XRD) measurement. In a casein which silicon crystallites are present in the silicon oxide particle,a diffraction peak derived from Si (111) is observed near 2θ=28.4° at atime of performing a powder X-ray diffraction (XRD) using a radiationsource of the CuKα radiation having a wavelength of 0.15406 nm.

A size of the silicon crystallite is preferably from 2.0 nm to 10.0 nm,and more preferably from 3.0 nm to 8.0 nm. In a case in which the sizeof the silicon crystallite is 15.0 nm or less, the silicon crystalliteis not apt to localize in a silicon oxide particle but rather apt todisperse in an entire of the silicon oxide particle. Therefore, lithiumions can diffuse easily in the silicon oxide particle so as tofacilitate achievement of excellent discharge capacity. In a case inwhich the size of the crystallite is 1.0 nm or more, a reaction betweena lithium ion and a silicon oxide can be well controlled so as tofacilitate achievement of excellent charge and discharge efficiency.

The size of the silicon crystallite is a size of a single crystal ofsilicon included in the silicon oxide particle and can be determinedusing the Scherrer equation based on the half width of a diffractionpeak near 2θ=28.4° derived from Si (111) obtained by a powder X-raydiffraction analysis using a radiation source of the CuKα radiationhaving a wavelength of 0.15406 nm.

A method to generate the silicon crystallite in the silicon oxideparticle is not particularly limited. For example, it can be generatedby subjecting the silicon oxide particle to a heat treatment in atemperature range of from 700° C. to 1300° C. under an inert atmosphereto cause the disproportionation (2SiO→Si+SiO₂). The heat treatment tocause disproportionation may be performed as the same process as thatfor the heat treatment to provide carbon to a surface of the siliconoxide particle.

The heat treatment conditions for causing the disproportionationreaction of the silicon oxide can be, for example, performance with thesilicon oxide in an inert atmosphere in a temperature range of 700° C.to 1300° C., preferably in a temperature range of 800° C. to 1200° C.From the viewpoint of generating a silicon crystallite with a desiredsize, the heat treatment temperature is preferably over 900° C., andmore preferably 950° C. or higher. The heat treatment temperature ispreferably less than 1150° C., and more preferably 1100° C. or lower.

(Mean Aspect Ratio)

The negative electrode active material has a mean value of an aspectratio (i.e., mean aspect ratio), which is represented by a ratio (S/L)of a major axis L and a minor axis S, of 0.45≤S/L≤1.

In general, when silicon oxide is used as a negative electrode activematerial, a large volume change occurs due to insertion and desorptionof lithium ions during charge and discharge. Therefore, when thecharging and discharging is repeated, the silicon oxide particles arecracked and micronized, and the electrode structure of the negativeelectrode using the silicon oxide particles is also destroyed and theconductive path may be cut. In the present disclosure, by setting themean aspect ratio of the negative electrode active material to be withinthe range of 0.45≤S/L≤1, the difference in volume change amount betweenthe expanded state and the contracted state as the electrode isaveraged, and collapse of the electrode structure is suppressed. It isconsidered that as a result thereof conduction between adjacentparticles becomes easy to be achieved even if the silicon oxideparticles expand and contract.

The mean aspect ratio of the negative electrode active material iswithin the range of 0.45≤S/L≤1, preferably within a range of 0.55≤S/L≤1,and more preferably within a range of 0.65≤S/L≤1. In a case in which themean aspect ratio of the negative electrode active material is 0.45 ormore, there is a tendency that the difference in volume change amountfor each region due to expansion and contraction as an electrode issmall, and the deterioration of cycle characteristics is suppressed.

The aspect ratio of the negative electrode active material is measuredby an observation using a scanning electron microscope (ScanningElectron Microscope, SEM). The mean aspect ratio is calculated as anarithmetic mean value of the aspect ratios obtained by arbitrarilyselecting 100 particles from an SEM image and measuring each of theseparticles.

The ratio (S/L) of the minor axis S to the major axis L of themeasurement target particle means the ratio of the minor axis (minimumdiameter)/major axis (maximum diameter) for a spherical particle, andthe ratio of the minor axis (minimum diameter or minimum diagonallength)/major axis (maximum diameter or maximum diagonal length) for ahexagonal plate-shaped or disk-shaped particle in the projected image ofthe particle observed from the thickness direction (observed with asurface corresponding to the thickness facing the front surface)respectively.

In a case in which the negative electrode active material contains aconductive particle described below, the conductive particle is excludedfrom the target of measurement of the mean aspect ratio.

In a case in which the negative electrode active material is obtainedthrough a heat treatment for a disproportionation reaction of siliconoxide, there may be a case that individual particles are agglomerated.It is meant that particles used in the calculation of the mean aspectratio in this case are particles of the smallest unit (primaryparticles) that can exist alone as particles.

The value of the mean aspect ratio of the negative electrode activematerial can be adjusted by, for example, pulverizing conditions inmanufacturing the negative electrode active material. A generally knownpulverizer can be used for pulverizing the negative electrode activematerial, and a pulverizer which can apply mechanical energy such asshear force, impact force, compression force, frictional force or thelike can be used without any particular limitation. Examples of thepulverizer include a pulverizer (ball mill, bead mill, vibration mill orthe like) which pulverizes using impact force and friction force bykinetic energy of pulverizing media, a pulverizer (jet mill or the like)which pulverizes raw material particles by effects of impact andfriction among particles caused by jetting high pressure gas of severalor more atmospheric pressures from a jetting nozzle and accelerating theraw material particles by this jet air flow, and a pulverizer (hammermill, pin mill, disc mill or the like) which pulverizes raw materialparticles by applying impact to the raw material particles by ahigh-speed rotating hammer, a pin, or a disc.

When the negative electrode active material is obtained through apulverizing process, the particle size distribution may be adjusted byperforming a classification process after pulverizing. A method of theclassification is not particularly limited, and may be selected from dryclassification, wet classification, sieving or the like. From theviewpoint of productivity, it is preferable to perform pulverization andclassification collectively. For example, a coupling system of j et milland cyclone allows the particles to be classified prior tore-agglomeration to conveniently obtain a particle size distributionhaving desired shape.

When necessary, for example, in a case in which the aspect ratio of thenegative electrode active material cannot be adjusted to a desired rangeonly by the pulverizing treatment, the negative electrode activematerial may be further subject to a surface modification treatmentafter the pulverization to adjust the aspect ratio. An apparatus forperforming the surface modification treatment is not particularlylimited. Examples thereof include mechanofusion systems, NOBILTA,hybridization systems and the like.

(Specific Surface Area and Moisture Adsorption Calculated from MoistureAdsorption)

The negative electrode active material has a specific surface areacalculated from moisture adsorption at 298 K of 6.5 m²/g or less, andpreferably 3.0 m²/g or less, and more preferably 2.0 m²/g or less. In acase in which the specific surface area calculated from moistureadsorption at 298 K is 6.5 m²/g or less, a decomposition reactionoccurring at an interface between the negative electrode active materialand an electrolyte can be suppressed, which tends to prevent degradationof high temperature storage characteristics. The specific surface areacalculated from moisture adsorption at 298 K may be 0.1 m²/g or more, ormay be 0.5 m²/g or more.

The amount of adsorption of moisture up to a relative pressure of 0.95at 298 K may be 8.5 cm³/g or less, and preferably 6.5 cm³/g or less, andmore preferably 3.0 cm³/g or less. In a case in which the amount ofadsorption of moisture up to a relative pressure of 0.95 at 298 K is 8.5cm³/g or less, a decomposition reaction occurring at an interfacebetween the negative electrode active material and an electrolyte can besuppressed, which tends to prevent degradation of high temperaturestorage characteristics. The amount of adsorption of moisture up to arelative pressure of 0.95 at 298 K is 1.0 cm³/g or more, or may be 1.5cm³/g or more.

The specific surface area calculated from moisture adsorption at 298 Kcan be calculated using a BET method from an adsorption isothermobtained from a moisture adsorption measurement at 298 K. The amount ofadsorption of moisture up to a relative pressure of 0.95 at 298 K can becalculated by measuring moisture adsorption up to a relative pressure of0.95 at 298 K using a multipoint method.

(Volume Mean Particle Size)

A volume mean particle diameter of the negative electrode activematerial is not particularly limited. For example, the volume meanparticle diameter is preferably from 0.1 μm to 20 μm, and morepreferably 0.5 μm to 10 μm. The volume mean particle diameter of thenegative electrode active material is D50% which is a particle diametercorresponding to 50% cumulative volume from a small particle diameterside in a volume-based particle size distribution curve. In a case inwhich the volume mean particle diameter is 0.1 μm or more, since thespecific surface area does not become too large, the increase in contactarea with the electrolyte is suppressed, and the charge/dischargeefficiency tends not to decrease. In a case in which the volume meanparticle diameter is 20 μm or less, unevenness on the electrode surfaceis less likely to occur, which tends to prevent a battery short circuit.Furthermore, since the diffusion distance of lithium from the surface ofthe particles to the interior does not become too long, the acceptanceof lithium is less likely to be reduced and charge/discharge efficiencyis less likely to be reduced.

For the measurement of the volume mean particle diameter, a known methodsuch as a laser diffraction particle size distributor can be employed.

(Specific Surface Area Calculated by Nitrogen Adsorption)

A specific surface area calculated by nitrogen adsorption at 77 K of thenegative electrode material is preferably from 0.1 m²/g to 10 m²/g, morepreferably from 0.5 m²/g to 5.0 m²/g, further preferably from 1.0 m²/gto 4.0 m²/g, and particularly preferably from 1.0 m²/g to 3.0 m²/g. In acase in which the specific surface area of the negative electrodematerial is 10 m²/g or less, increase in the initial irreversiblecapacity of a lithium ion secondary battery produced therewith tends tobe suppressed. Further, increase in the consumption of a binder forproducing a negative electrode can be suppressed. In a case in which thespecific surface area of the negative electrode material is 0.1 m²/g ormore, the contact area of the negative electrode material with anelectrolyte solution is sufficiently made and the charge/dischargeefficiency tends to increase. Measurement of the specific surface areacan be performed by a conventionally known method such as a BET method(a nitrogen gas adsorption method) or the like.

The negative electrode active material preferably has a ratio(D10%/D90%) of 0.1 or more, more preferably 0.2 or more, and stillpreferably 0.3 or more, in which D90% is a particle diametercorresponding to 90% cumulative from a smaller particle diameter side ina cumulative volume distribution curve obtained by a laserdiffraction/scattering method and D10% is a particle diametercorresponding to 10% cumulative from a smaller particle diameter side inthe cumulative volume distribution curve. In a case in which the valueof D10%/D90% of the negative electrode active material is 0.1 or more, adifference in an amount of change in expansion and contraction of anelectrode becomes small, and deterioration of the cycle characteristictends to be suppressed. The ratio D10%/D90% of the negative electrodeactive material may be 1.0 or less, preferably 0.8 or less, and morepreferably 0.6 or less.

The value of D10%/D90% of the negative electrode active material is anindex relating to the width and narrowness of a particle sizedistribution of the negative electrode active material, and a largevalue of D10%/D90% means that the particle size distribution of thenegative electrode active material is narrow.

The D90% and D10% of the negative electrode active material arerespectively obtained as a particle diameter when a cumulative volumefrom a small particle diameter side is 90% and as a particle diameterwhen a cumulative volume from a small particle diameter side is 10%, ina volume-based particle size distribution measured by a laserdiffraction/scattering method using a sample in which the negativeelectrode active material is dispersed in water.

(Organic Substance)

The negative electrode active material in the present disclosure may becoated with an organic substance. In a case in which the negativeelectrode active material is coated by the organic substance, theinitial discharge capacity, the initial charge/discharge efficiency, andthe recovery rate after charge/discharge tend to be further improved.This is considered to be because coating an organic substance causesreduction of the specific surface area of the negative electrode activematerial to result in suppression of the reaction of the negativeelectrode active material with the electrolyte solution. The organicsubstance contained in the negative electrode active material may beonly one kind or two or more kinds thereof.

A content of the organic substance is preferably from 0.1% by mass to5.0% by mass with respect to a total mass of the negative electrodeactive material. In a case in which the content of the organic substanceis within the above range, an effect of improving the recovery rateafter charging/discharging tends to be sufficiently obtained whilesuppressing the decrease in conductivity. The content of the organicsubstance with respect to the total mass of the negative electrodeactive material is more preferably from 0.2% by mass to 3.0% by mass andfurther preferably from 0.3% by mass to 1.0% by mass.

Whether or not the negative electrode active material contains theorganic substance can be observed by, for example, heating the negativeelectrode active material which is sufficiently dried to a temperatureequal to or higher than the temperature at which the organic substancedecomposes but lower than a temperature at which carbon decomposes, forexample, 300° C., and measuring a mass of the negative electrode activematerial after the organic substance decomposes. Specifically, it can bedetermined that the negative electrode active material contains theorganic substance if a rate of change in mass represented by{(A−B)/A}×100 is 0.1% or more, provided that the mass of the negativeelectrode active material before heating is A(g) and the mass of thenegative electrode active material after heating is B(g).

The rate of change in mass is preferably from 0.1% to 5.0%, and morepreferably 0.3% to 1.0%. In a case in which the rate of change is 0.1%or more, a sufficient quantity of the organic substance exists on asurface of the SiO—C particle, so that the effects due to inclusion ofthe organic substance tend to be sufficiently obtained.

A kind of the organic substance is not particularly limited. Forexample, at least one selected from the group consisting of a starchderivative having C₆H₁₀O₅ as a unit structure thereof, a viscouspolysaccharide having C₆H₁₀O₅ as a unit structure thereof, awater-soluble cellulose derivative having C₆H₁₀O₅ as a unit structurethereof, polyuronides, and a water-soluble synthetic resin can bementioned.

Specific examples of the starch derivative having C₆H₁₀O₅ as a unitstructure thereof include hydroxyalkyl starches such as acetic acidstarch, phosphate starch, carboxymethyl starch, and hydroxyethyl starch.Specific examples of the viscous polysaccharide having C₆H₁₀O₅ as a unitstructure thereof include pullulan, dextrin, and the like. Specificexamples of the water-soluble cellulose derivatives having C₆H₁₀O₅ as aunit structure thereof include carboxymethylcellulose, methylcellulose,hydroxyethylcellulose, hydroxypropylcellulose and the like. Examples ofthe polyuronide include pectic acid, alginic acid and the like. Examplesof the water-soluble synthetic resin include a water-soluble acrylicresin, a water-soluble epoxy resin, a water-soluble polyester resin, awater-soluble polyamide resin and the like, and more specific examplesthereof include polyvinyl alcohol, polyacrylic acid, polyacrylic acidsalt, polyvinyl sulfonic acid, polyvinyl sulfonic acid salt, poly4-vinyl phenol, poly 4-vinyl phenol salt, polystyrene sulfonic acid,polystyrene sulfonic acid salt, polyaniline sulfonic acid and the like.The organic substance may be used in a form of a metal salt, an alkyleneglycol esters or the like.

From the viewpoint of reducing the specific surface area of the negativeelectrode active material, it is preferable that the organic substanceis in a state in which a part or an entire of a surface of the SiO—Cparticle (in a case in which the conductive particle to be describedbelow is present on the surface of the SiO—C particle, the surfacethereof) is coated.

There are no particular restrictions on the manner in which the organicsubstance is present on a part or an entire of the surface of the SiO—Cparticle. For example, the organic substance can be attached to theSiO—C particle by introducing the SiO—C particle into a liquid in whichthe organic substance is dissolved or dispersed and agitating the liquidas required. Thereafter, the SiO—C particle to which the organicsubstance adheres are taken out from the liquid and dried as required,whereby SiO—C particle to which the organic substance adheres can beobtained.

In the above method, a temperature of the liquid at the time ofagitating is not particularly limited, and can be selected, for example,from 5° C. to 95° C. A temperature at the time of drying is notparticularly limited, and can be selected, for example, from 50° C. to200° C. A content of the organic substance in the solution is notparticularly limited, and can be selected, for example, from 0.1% bymass to 20% by mass.

(Conductive Particle)

The negative electrode active material in the present disclosure (SiObased negative electrode active material) disclosure may contain aconductive particle if needed. In a case in which the negative electrodeactive material contains the conductive particle, conduction can beeasily made by the conductive particles coming into contact with eachother even if expansion and contraction of the silicon oxide particlesoccur. In addition, the resistance value of the entire negativeelectrode active material tends to be reduced. As a result, a decreasein capacity due to repetition of charge and discharge is suppressed, andthe cycle characteristics tend to be satisfactorily maintained.

From the viewpoint of ensuring electrical continuity via contacts of thenegative electrode active materials with each other, it is preferablethat the conductive particle exists on the surface of the SiO—Cparticle.

A kind of the conductive particle is not particularly limited. Forexample, at least one selected from the group consisting of granulargraphite and carbon black is preferable, and granular graphite ispreferable from the viewpoint of improving cycle characteristics.Examples of the granular graphite include particles of artificialgraphite, particles of natural graphite, and particles of MC (mesophasecarbon). Examples of the carbon black include acetylene black, Ketjenblack, thermal black, furnace black and the like, and acetylene black ispreferable from the standpoint of conductivity.

The granular graphite preferably has higher crystallinity than carbonpresent on the surface of the silicon oxide particles from the viewpointof improving both the battery capacity and the charge/dischargeefficiency. Specifically, the particulate graphite preferably has a meaninterplanar spacing (d₀₀₂) measured according to the Gakushin method offrom 0.335 nm to 0.347 nm, more preferably from 0.335 nm to 0.345 nm,more preferably from 0.335 nm to 0.340 nm, and particularly preferablyfrom 0.335 nm to 0.337 nm. In a case in which the mean interplanarspacing of the granular graphite is 0.347 nm or less, the crystallinityof the granular graphite is high, and both the battery capacity and thecharge/discharge efficiency tend to be improved. On the other hand,since the theoretical value of a mean interplanar spacing of thegraphite crystal is 0.335 nm, in a case in which the mean interplanarspacing of the granular graphite is close to this value, both thebattery capacity and the charge/discharge efficiency tend to beimproved.

A shape of the granular graphite is not particularly limited and it maybe flat graphite or spherical graphite. From the standpoint of improvingcycle characteristics, flat graphite is preferable.

Flat graphite in the present disclosure means graphite an aspect ratioof which is not 1, i.e., the length of the minor axis and the length ofthe major axis thereof are not equal. Examples of the flat graphiteinclude graphite having a shape of a scale, a flake, a lump or the like.

An aspect ratio of the conductive particle is not particularly limited,and a mean value of the aspect ratio is preferably 0.3 or less, and morepreferably 0.2 or less, from the viewpoint of easiness of ensuring theconduction between the conductive particles and improvement in cyclecharacteristics.

The aspect ratio of the conductive particle is a value measured byobservation with a SEM. Specifically, it is a value calculated as B/Aprovided that a length in the major axis direction is A and a length inthe minor axis direction (in the case of flat graphite, it means thelength in the thickness direction) is B for each of 100 arbitrarilyselected conductive particles in a SEM image. The mean value of theaspect ratio is an arithmetic mean value of the aspect ratio of 100conductive particles.

The conductive particle may be a primary particle (single particle) or asecondary particle (granulated particle) formed from a plurality ofprimary particles. The flat graphite may be a porous graphite particle.

A content of the conductive particle with respect to a total mass of thenegative electrode active material is preferably from 1.0% by mass to10.0% by mass, more preferably 2.0% by mass to 9.0% by mass, and stillmore preferably 3.0% by mass to 8.0% by mass, from the viewpoint ofimproving the cycle characteristics.

The content of the conductive particle can be determined by, forexample, a high-frequency furnace combustion-infrared absorptionspectrometry. In the high-frequency furnace combustion-infraredabsorption spectrometry, for example, a sulfur/carbon simultaneousanalyzer (CSLS600, Japan LECO Co., Ltd.) can be used. Since thismeasurement provides a result including a content of carbon in the SiO—Cparticle, the content of carbon may be separately measured andsubtracted from the obtained content.

A method for manufacturing the negative electrode active materialcontaining the conductive particle is not particularly limited, and mayinclude a wet method and a dry method.

Examples of a method of producing the negative electrode active materialcontaining a conductive particle by a wet method include a method whichincludes adding the SiO—C particle to a particle dispersion liquid inwhich conductive particles are dispersed in a dispersion medium,agitating the particle dispersion liquid, and then removing thedispersion medium using a dryer or the like. The dispersion medium usedtherein is not particularly limited, and water, an organic solvent orthe like can be used. The organic solvent may be a water-soluble organicsolvent such as an alcohol or may be a water-insoluble organic solvent.The dispersing medium may contain a dispersant from the viewpoint ofenhancing dispersibility of the conductive particles and increasinguniform adherence of the conductive particles to the surface of theSiO—C particle. The dispersant can be selected according to the type ofdispersion medium used. For example, in a case in which the dispersionmedium is a water-based medium, carboxymethylcellulose is preferable asthe dispersant from the viewpoint of dispersion stability.

Examples of a method of producing the negative electrode active materialcontaining the conductive particle by the dry method include a methodwhich includes adding the conductive particle together with a carbonsource for carbon when the carbon source is applied to a surface of thesilicon oxide particle. Specific examples thereof include a methodincluding mixing the carbon source and the conductive particle with thesilicon oxide particle and applying mechanical energy (for example, amechanochemical treatment).

If necessary, classification of the obtained negative electrode activematerial may be further performed. The classification process can beperformed using a sieving machine or the like.

<Negative Electrode Active Material for Lithium Ion Secondary Battery(Second Embodiment)>

The negative electrode active material for a lithium ion secondarybattery in the present disclosure includes silicon oxide particles, eachof which has carbon on at least a portion of its surface, in which: aratio (P_(Si)/P_(SiO2)) of an intensity of an X-ray diffraction peak at2θ of from 27° to 29°, which is derived from Si, to an intensity of anX-ray diffraction peak at 2θ of from 20° to 25°, which is derived fromSiO₂, is within a range of from 1.0 to 2.6, when CuKα radiation having awavelength of 0.15406 nm is used as a radiation source; and an amount ofadsorption of moisture up to a relative pressure of 0.95 at 298 K is 8.5cm³/g or less.

Details and preferable aspects of the negative electrode active materialand its components of the second embodiment are the same as the detailsand preferable aspects of the negative electrode active material and itscomponents of the first embodiment, except that the specific surfacearea calculated from moisture adsorption at 298 K is not limited.

The amount of adsorption of moisture up to a relative pressure of 0.95at 298 K may be 8.5 cm³/g or less, preferably 6.5 cm³/g or less, andmore preferably 3.0 cm³/g or less. In a case in which the amount ofadsorption of moisture up to a relative pressure of 0.95 at 298 K is 8.5cm³/g or less, a decomposition reaction occurring at an interfacebetween the negative electrode active material and an electrolyte can besuppressed, which tends to prevent degradation of high temperaturestorage characteristics. The amount of adsorption of moisture up to arelative pressure of 0.95 at 298 K may be 1.0 cm³/g or more, or may be1.5 cm³/g or more.

The amount of adsorption of moisture up to a relative pressure of 0.95at 298 K can be calculated in the same manner as described above.

An example of a configuration of the negative electrode active materialis explained hereinafter with referring to the Figures.

FIGS. 1 to 5 are schematic sectional views illustrating examples of astructure of the negative electrode active material, respectively. InFIG. 1, carbon 10 covers an entire surface of a silicon oxide particle20. In FIG. 2, carbon 10 covers an entire surface of a silicon oxideparticle 20, although a thickness thereof is non-uniform. In FIG. 3,carbon 10 is present on a part of a surface of a silicon oxide particle20, and thus the surface of the silicon oxide particle 20 is partiallyexposed. In FIG. 4, particles of carbon 10 having a smaller particlesize than the silicon oxide particle 20 are present on a surface of asilicon oxide particle 20. FIG. 5 is a variant of FIG. 4, in which theparticle of carbon 10 is scale-shaped. In FIGS. 1 to 5, a shape of thesilicon oxide particle 20 is schematically represented as spherical(circle as a cross-sectional shape), but the shape may be spherical,block-shaped, scale-shaped, polygonal (angular shape) in cross-sectionalshape, or the like.

Each of FIGS. 6A and 6B is an enlarged cross sectional viewschematically illustrating a portion of the negative electrode activematerial shown in FIGS. 1 to 3. FIG. 6A illustrates an embodiment of astate of the carbon 10 in the negative electrode active material, andFIG. 6B illustrates another embodiment of the state of the carbon 10 inthe negative electrode active material. Regarding FIGS. 1 to 3, carbon10 may be in a state in which it forms a continuous layer as shown inFIG. 6A, or may be in a state of carbon granules 12, which are granulesformed of the carbon 10, as shown in FIG. 6B. In FIG. 6B, while thegranules 12 formed of the carbon 10 are shown in the state in which theoutlines thereof are remained, the granules 12 may be connected with oneanother. When the granules 12 are connected with one another, the carbon10 may be in a state in which, as shown in FIG. 6A, it forms acontinuous layer, which may include a void in a part thereof.

In a case in which carbon 10 is particulate, particles of carbon 10 maybe partially present on the surface of silicon oxide particle 20, andthe surface of silicon oxide particle 20 may not be covered withparticles of carbon 10 in part as shown in FIG. 4, or particles ofcarbon 12 may be present on the entire surface of silicon oxide particle20, as shown in FIG. 6B.

If necessary, the negative electrode active material of the presentdisclosure (SiO-based negative electrode active material) may be used incombination with a carbon-based negative electrode active materialconventionally known as an active material for a negative electrode of alithium ion secondary battery. An effect of improving the charge anddischarge efficiency, an effect of improving the cycle characteristics,an effect of suppressing the expansion of the electrode and the like areobtained depending on a kind of a carbon-based negative electrode activematerial used in combination. The carbon-based negative electrode activematerial to be used in combination with the negative electrode activematerial of the present disclosure may be only one kind or two or morekinds thereof.

A general carbon material known as a negative electrode active materialfor a lithium ion secondary battery may be used as the carbon-basednegative electrode active material. Examples of the carbon-basednegative electrode active material include a negative electrode activematerial formed of a carbon material such as: a natural graphite such asflake-shaped natural graphite or spherical natural graphite obtained byspheroidizing flake-shaped natural graphite; an artificial graphite; oran amorphous carbon. The carbon-based negative electrode active materialmay have carbon (the carbons described above) present on a part of thesurface thereof or the entire surface thereof.

In a case in which the negative electrode active material of the presentdisclosure is used in combination with the carbon-based negativeelectrode active material, a ratio (A:B) of the negative electrodeactive material of the present disclosure (A) to the carbon-basednegative electrode active material (B) can be appropriately adjusted inaccordance with the purpose. For example, from the viewpoint of aneffect of suppressing the expansion of the electrode, the ratio ispreferably from 0.1:99.9 to 20:80, more preferably from 0.5:99.5 to15:85, and still more preferably from 1:99 to 10:90, based on the mass.

<Negative Electrode for Lithium Ion Secondary Battery>

A negative electrode for a lithium ion secondary battery (hereinafter,sometimes abbreviated to a “negative electrode”) of the presentdisclosure includes: a current collector; and a negative electrodematerial layer that is provided on or above the current collector andthat includes the above-described negative electrode active material.

The negative electrode may be produced, for example, by forming anegative electrode material layer on or above a current collector usinga composition containing the negative electrode active materialdescribed above.

Examples of the composition containing the negative electrode activematerial include a mixture of an organic binder, a solvent, a thickener,an electroconductive auxiliary material, a carbon-based negativeelectrode active material, and/or the like in addition to the negativeelectrode active material.

Specific examples of the organic binder include styrene-butadienecopolymers; (meth)acrylic copolymers obtained by copolymerization of anethylenic unsaturated carboxylic acid ester (such asmethyl(meth)acrylate, ethyl(meth)acrylate, butyl(meth)acrylate,(meth)acrylonitrile, or hydroxyethyl(meth)acrylate) and an ethylenicunsaturated carboxylic acid (such as acrylic acid, methacrylic acid,itaconic acid, fumaric acid, or maleic acid); and polymer compounds suchas polyvinylidene fluoride, polyethylene oxide, polyepichlorohydrin,polyphosphazene, polyacrylonitrile, polyimide, or polyamide imide. Here,the term “(meth)acrylate” means “acrylate” and “methacrylate”corresponding thereto. The same applies to “(meth)acrylic copolymer” andother similar expressions. The organic binder may be one dispersed ordissolved in water, or one dissolved in an organic solvent such asN-methyl-2-pyrrolidone (NMP). Only one kind of the organic binder may beused, or alternatively, a combination of two or more kinds of theorganic binder may be used.

In view of adhesiveness, among the organic binders, an organic binderhaving polyacrylonitrile, polyimide, or polyamide imide as a mainskeleton thereof is preferable, and from the viewpoints of a low heattreatment temperature during the production of a negative electrode andexcellent electrode flexibility, an organic binder havingpolyacrylonitrile as a main skeleton thereof is more preferable.Examples of the organic binder having polyacrylonitrile as a mainskeleton thereof include one in that an acrylic acid for impartingadhesiveness and a straight chain ether group for imparting flexibilityare added to a polyacrylonitrile skeleton.

A content of the organic binder in a negative electrode material layeris preferably from 0.1% by mass to 20% by mass, more preferably from0.2% by mass to 20% by mass, and still more preferably from 0.3% by massto 15% by mass. In a case in which the content of the organic binder ina negative electrode material layer is 0.1% by mass or more, excellentadhesiveness can achieved, and destruction of a negative electrode byexpansion and constriction in charging and discharging tends to besuppressed. Meanwhile, in a case in which the content is 20% by mass orless, increase of electrode resistance tends to be suppressed.

Specific examples of the thickener include carboxymethyl cellulose,methylcellulose, hydroxymethyl cellulose, ethyl cellulose, polyvinylalcohol, polyacrylic acid (polyacrylate), oxidized starch,phosphorylated starch, casein and the like. Only one kind of thethickener may be used, or alternatively, a combination of two or morekinds of the thickener may be used.

Specific examples of the solvent include N-methylpyrrolidone, dimethylacetamide, dimethylformamide, γ-butyrolactone and the like. Only onekind of the solvent may be used, or alternatively, a combination of twoor more kinds of the solvent may be used.

Specific examples of the electroconductive auxiliary material includecarbon black, acetylene black, an oxide having electrical conductivity,a nitride having electrical conductivity and the like. Only one kind ofthe electroconductive auxiliary material may be used, or alternatively,a combination of two or more kinds of the electroconductive auxiliarymaterial may be used. A content of the electroconductive auxiliarymaterial is preferably from 0.1% by mass to 20% by mass with respect tothe negative electrode material layer.

Examples of a material of the current collector include aluminum,copper, nickel, titanium, stainless steel, a porous metal (a foamedmetal), and a carbon paper. Examples of a shape of the current collectorinclude a foil form, a perforated foil form, and a mesh form.

Examples of a method of forming the negative electrode material layer onthe current collector using the composition containing the negativeelectrode active material include: a method including applying a coatingliquid including the negative electrode active material to the currentcollector, removing therefrom volatile substances such as a solvent, andsubjecting the resultant to press-forming; and a method includingintegrating the negative electrode material layer which is made in asheet-like shape, pellet-like shape or the like and the currentcollector; and the like.

Examples of the method of applying the coating liquid to the currentcollector include a metal mask printing method, an electrostatic coatingmethod, a dip coating method, a spray coating method, a roll coatingmethod, a doctor blade method, a gravure coating method, and a screenprinting method. A pressure treatment after the application may beperformed by a flat-plate press, a calender roll, or the like.

Integration of the negative electrode material layer and the currentcollector may be carried out by rolling, pressing, or a combinationthereof.

The negative electrode material layer formed on the current collector orthe negative electrode layer integrated with the current collector maybe subjected to a heat treatment which depends on the organic binderused. For example, in a case in which an organic binder having apolyacrylonitrile as its main skeleton is used, the heat treatment ispreferably carried out at a temperature of from 100° C. to 180° C., andin a case in which an organic binder having a polyimide orpolyamide-imide as its main skeleton is used, the heat treatment ispreferably carried out at a temperature of from 150° C. to 450° C.

By the heat treatment, the solvent is removed, the strength is highlyintensified through the curing of the organic binder, and theadhesiveness between the negative electrode active materials and theadhesiveness between the negative electrode active material and thecurrent collector can be improved. These heat treatments are preferablycarried out in an inert atmosphere, such as helium, argon, or nitrogen,or in a vacuum atmosphere, in order to prevent oxidization of thecurrent collector during the treatment.

The negative electrode layer may preferably be pressed (pressuretreatment) before the heat treatment. By the pressure treatment, itselectrode density can be controlled. The electrode density is preferablyfrom 1.25 g/cm³ to 1.9 g/cm³, more preferably from 1.5 g/cm³ to 1.85g/cm³, and still more preferably from 1.6 g/cm³ to 1.8 g/cm³. The higherthe electrode density is, the more the volumetric capacity of thenegative electrode tends to be improved and further the adhesivenessbetween negative electrode active materials and the adhesiveness betweenthe negative electrode active material and the current collector tendsto be improved.

<Lithium Ion Secondary Battery>

A lithium ion secondary battery according to the present disclosureincludes: a positive electrode; the negative electrode described above;and an electrolyte.

The lithium ion secondary battery may be prepared by, for example,oppositely disposing in a cell casing the negative electrode and thepositive electrode with a separator therebetween, and injecting thereinan electrolytic solution obtained by dissolving an electrolyte to anorganic solvent.

In the lithium ion secondary battery of the present disclosure, a solidelectrolyte may be used as an electrolyte. Since a solid electrolyte canalso serve as a separator, when a solid electrolyte is used as anelectrolyte, a lithium ion secondary battery does not need to use aseparator.

The positive electrode may be obtained similarly as the negativeelectrode, by forming a positive electrode material layer on the surfaceof a current collector. As a current collector for the positiveelectrode, a current collector similar to one usable for the negativeelectrode may be used.

A material to be used for the positive electrode (also referred to as a“positive electrode material”) may be any compound as long as it enablesdoping or intercalation of a lithium ion, and examples thereof includelithium cobaltate (LiCoO₂), lithium nickelate (LiNiO₂), and lithiummanganate (LiMnO₂).

The positive electrode may be produced by, for example, preparing apositive electrode coating liquid by mixing the positive electrodematerial, an organic binder such as polyvinylidene fluoride, and amedium such as N-methyl-2-pyrrolidone or γ-butyrolactone, applying thepositive electrode coating liquid to at least one surface of a currentcollector such as aluminum foil, and removing the medium by drying,followed by, if necessary, a pressure treatment.

An electroconductive auxiliary material may be added to the positiveelectrode coating liquid. Examples of the electroconductive auxiliarymaterial include carbon black, acetylene black, an oxide havingelectrical conductivity or a nitride having electrical conductivity.Only one kind of the electroconductive auxiliary material may be used,or alternatively, a combination of two or more kinds of theelectroconductive auxiliary material may be used.

Examples of the electrolyte include LiPF₆, LiClO₄, LiBF₄, LiClF₄,LiAsF₆, LiSbF₆, LiAlO₄, LiAlCl₄, LiN(CF₃SO₂)₂, LiN(C₂F₅SO₂)₂,LiC(CF₃SO₂)₃, LiCl, and LiI.

Examples of the organic solvent which dissolves the electrolyte includepropylene carbonate, ethylene carbonate, diethyl carbonate, ethyl methylcarbonate, vinyl carbonate, γ-butyrolactone, 1,2-dimethoxyethane, and2-methyltetrahydrofuran.

Examples of the separator include a paper separator, a polypropyleneseparator, a polystyrene separator, and a glass fiber separator.

A method of producing the lithium ion secondary battery is notparticularly limited. For example, a cylindrical lithium ion secondarybattery may be produced by the processes below. First, two electrodes ofthe positive electrode and the negative electrode are wound togetherwith the separator placed therebetween. The obtained wound group in aspiral shape is inserted in a cell casing, and a tab terminal, which hasbeen welded to a current collector of the negative electrode in advance,is welded to the bottom of the cell casing. An electrolytic solution isintroduced into the obtained cell casing, and a tab terminal, which hasbeen welded to a current collector of the positive electrode in advance,is welded to the lid of the cell casing. The lid is arranged on the topof the cell casing with an insulating gasket disposed therebetween, andthe portion at which the lid contacts with the cell casing are swaged soas to seal them, thereby obtaining a lithium ion secondary battery.

The shape of the lithium ion secondary battery is not particularlylimited, and examples thereof include a paper lithium ion secondarybattery, a button lithium ion secondary battery, a coin lithium ionsecondary battery, a layered lithium ion secondary battery, acylindrical lithium ion secondary battery, and a rectangular lithium ionsecondary battery.

The negative electrode active material according to the presentdisclosure is not limited to an application for a lithium ion secondarybattery, and it may be applied generally to an electrochemical apparatusemploying lithium-ion intercalation/deintercalation as a charge anddischarge mechanism.

EXAMPLES

Hereinafter, the embodiments are described more specifically withreference to Examples, but the embodiments are not limited to theexamples. Here, “%” is based on mass unless otherwise specified.

Example 1

(Preparation of Negative Electrode Active Material)

Oxidized silicon having a bulk-shape (Kojundo Chemical Lab. Co., Ltd,standard 10 mm to 30 mm square) was coarsely ground in a mortar, therebyobtaining silicon oxide particles. The silicon oxide particles werefurther pulverized with a jet mill (LABO TYPE, manufactured by NipponPneumatic Mfg. Co., Ltd.), and then the particle diameter thereof wasregulated using a 300-M (300-mesh) test screen, thereby obtainingsilicon oxide particles having a volume mean particle diameter (D50%) of5 μm. The mean particle diameter was measured by a method shown below.

<Measurement of Volume Mean Particle Diameter>

The measurement sample (5 mg) was added to a 0.01% by mass aqueoussolution of surfactant (ETHOMEEN T/15, Lion Corporation), and themixture was dispersed using a vibrational stirrer. The obtaineddispersion was placed in a sample vessel of a laser diffraction particlesize distribution measurement apparatus (SALD 3000J, ShimadzuCorporation), and measurement was carried out with a laserdiffractometry method while circulating using a pump under an ultrasonictreatment. The measurement conditions are shown below. A particlediameter at which a cumulative volume reached 50% (D50%) in the obtainedparticle size distribution was defined as a mean particle diameter. Inthe following Examples, the measurements of the mean particle diameterswere performed in a similar manner.

Light source: Red-color semiconductor laser (690 nm)

Absorbance: 0.10 to 0.15

Refractive index: 2.00 to 0.20

A carbon film was formed on the surface of silicon oxide particles bychemical vapor deposition on silicon oxide particles with a volume meanparticle diameter (D50%) of 5 μm, obtained after grinding process ofsilicon oxide, using the following conditions.

1000 g of silicon oxide particles were prepared in a batch heatingfurnace (rotary kiln furnace). Next, the temperature was raised to 950°C. at 300° C./hour and held at 950° C., and then a mixture of acetylenegas (carbon source) and nitrogen gas flowed in at 10 L/min (partialpressure of acetylene gas: 10%) for 2 hours to carry out a chemicaldeposition treatment. After the treatment, the temperature was lowered,and a product of the chemical deposition treatment was obtained. Theabove-described heat treatment was carried out under the conditionswhere the disproportionation reaction of silicon oxides occurred.

The obtained heat-treated product was ground in a mortar, and furthersubjected to sieving with a 300-M (300-mesh) test screen, therebyobtaining a negative electrode active material (SiO—C particle), inwhich carbon covers surfaces of the silicon oxide particles. A volumemean particle diameter (D50%) of the negative electrode active materialwas measured in a similar manner to that for the silicon oxideparticles. Further, D10% and D90% were measured, and a value ofD10%/D90% were calculated therefrom.

<Measurement of Carbon Content>

A content of carbon in the negative electrode active material wasmeasured by a high-frequency furnace combustion-infrared absorptionspectrometry. The high-frequency furnace combustion-infrared absorptionspectrometry is an analysis method in which a sample is heated andcombusted in a high-frequency furnace under oxygen stream to convertcarbon and sulfur in the sample into CO₂ and SO₂, respectively, and theproducts are quantified with an infrared absorption method. Themeasurement apparatus, the measurement condition, and the like are asfollows.

Apparatus: sulfur/carbon simultaneous analyzer (CSLS600, LECO JapanCorporation)

Frequency: 18 MHz

High-frequency output: 1600 W

Sample mass: approximately 0.05 g

Analysis time: use in auto mode of the set mode of the apparatus

Combustion improver: Fe+W/Sn

Standard sample: LECO 501-024 (C: 3.03%±0.04, S: 0.055%±0.002) 97

Number of measurement: two times (a value of a content ratio shown inTable is a mean value of two measurements)

<Measurement of Size of Silicon Crystallite>

A size of a silicon crystallite was measured by measuring an intensityof an X-ray diffraction peak of the negative electrode active materialusing a powder X-ray diffractometer (MULTIFLEX (2 kW), RigakuCorporation). Specifically, it was determined by a Scherrer equationbased on a half-value width of a peak at 2θ=about 28.4° derived from acrystal face of Si (111). The measurement condition is as follows.

Radiation source: CuKα radiation (wavelength: 0.15406 nm)

Measurement range: 2θ=10° to 40°

Step width of sampling: 0.02°

Scan speed: 1°/min

Tube current: 40 mA

Tube voltage: 40 kV

Divergence slit: 1°

Scatter slit: 1°

Light receiving slit: 0.3 mm

The obtained profile was subject to removal of the background (BG) andseparation of the peak using a structure analyzing software (JADE 6,Rigaku Corporation.) supplied with the above apparatus in accordancewith the following settings.

[Removal of Kα2 Peak and Removal of Background]

Kα1/Kα2 intensity ratio: 2.0

Deviation (σ) of BG curve from BG point: 0.0

[Designation of Peak]

Peak derived from Si (111): 28.4°±0.3°

Peak derived from SiO₂: 21°±0.3°

[Separation of Peak]

Profile shape function: Pseudo-Voigt

Fixed background

The half-value width of the peak derived from Si (111) calculated by thestructure analyzing software in accordance with the above settings wasread, and the size of the silicon crystallite was calculated by thefollowing Scherrer equation.D=Kλ/B cos θB=(B _(obs) ² −b ²)^(1/2)

D: Size (nm) of crystallite

K: Scherrer constant (0.94)

λ: Wavelength of irradiation source (0.15406 nm)

θ: Peak angle of measured half-value width

B_(obs): Half-value width (the measured value obtained using thestructure analyzing software)

b: Measured half-value width of standard silicon (Si)

<Measurement of X-Ray Diffraction Peak Intensity Ratio(P_(Si)/P_(SiO2))>

The negative electrode active material was analyzed using a powder X-raydiffractometer (MultiFlex (2 kW), Rigaku Corporation) in a similarmanner to that described above. A ratio (P_(Si)/P_(SiO2)) of anintensity of an X-ray diffraction peak at 2θ of from 27° to 29° derivedfrom Si to an intensity of an X-ray diffraction peak at 2θ of from 20°to 25° derived from SiO₂ was calculated with respect to the negativeelectrode active material.

<Measurement of Mean Aspect Ratio>

A mean aspect ratio of each negative electrode active material wascalculated by the method described above using a SEM device (TM-1000,Hitachi High Technologies, Ltd.).

For the negative electrode active material containing the conductiveparticle described below, only SiO—C particles were selected byEDX-based elemental analysis in advance, and the mean aspect ratio wascalculated.

<Measurement of R Value>

An R Value was calculated from a spectrum measured by using a Ramanspectrum measurement apparatus (type NSR-1000, JASCO Corporation). Themeasurement conditions are as follows.

Laser wavelength: 532 nm

Irradiation intensity: 1.5 mW (the value measured with a laser powermonitor)

Irradiation time: 60 seconds

Irradiation area: 4 μm²

Measurement range: 830 cm⁻¹ to 1940 cm⁻¹

Base line: 1050 cm⁻¹ to 1750 cm⁻¹

A wavenumber of the obtained spectrum was corrected based on acalibration curve determined by a difference between the wavenumber ofthe respective peaks obtained by measuring a standard substance indene(Wako first grade, Wako Pure Chemical Industries) under the samecondition as above and the wavenumber of the theoretical value of therespective peaks of indene.

A peak strength occurred at near 1360 cm⁻¹ in the profile obtained afterthe correction was defined as I_(d), and a peak strength occurred atnear 1580 cm⁻¹ in the profile obtained after the correction was definedas I_(g). A ratio of the both peak intensities I_(d)/I_(g) (D/G) wasdetermined as the R value.

<Measurement of N₂ Specific Surface Area: Specific Surface AreaCalculated from Nitrogen Adsorption>

After vacuum drying a negative electrode active material at 200° C. for2 hours, nitrogen adsorption at liquid nitrogen temperature (77 K) wasmeasured by the multipoint method using a high-speed specific surfacearea/pore size analyzer (ASAP2020, Micromeritix Japan Ltd.), and thespecific surface area of the negative electrode active material wascalculated by a BET method (relative pressure range: from 0.05 to 0.2).

<Measurement of H₂O Specific Surface Area: Specific Surface AreaCalculated from moisture Adsorption>

After vacuum drying a negative electrode active material at 100° C. for2 hours, moisture adsorption at 298 K was measured by the multipointmethod using a high precision fully automated gas adsorption measurementdevice (BELSORP18, MicrotracBEL Corp.), and the specific surface area ofthe negative electrode active material was calculated by a BET method.

<H₂O Adsorption Amount>

After vacuum drying a negative electrode active material at 100° C. for2 hours, moisture adsorption up to a relative pressure of 0.95 at 298 Kwas measured by a multipoint method using a high precision fullyautomated gas adsorption measurement device (BELSORP18, MicrotracBELCorp.), and the total adsorption amount was calculated.

(Production of Negative Electrode)

To powder of negative electrode active material (79.0% by mass), powderof Ketjen Black (6.0% by mass) as a conductive aid and an organic binder(15.0% by mass) which has polyacrylonitrile as a main skeleton andacrylic acid and a linear ether group as a binder were added, and thenthe mixture was kneaded to prepare a composition for a negativeelectrode. The composition for forming a negative electrode was appliedto a glossy surface of an electrolytic copper foil such that theapplication amount is 2.5 mg/cm², subjected to a predrying treatment at90° C. for 2 hours, and then a density of the resultant was adjusted to1.30 g/cm³ by roll pressing. Subsequently, the resultant was dried at120° C. for 4 hours in a vacuum atmosphere, thereby obtaining a negativeelectrode.

Production of Lithium Ion Secondary Battery

A 2016-type coin cell was produced using the above-obtained negativeelectrode, a metal lithium as a counter electrode, a mixed liquid of 1MLiPF₆ containing ethyl carbonate (EC), diethyl carbonate (DEC) and ethylmethyl carbonate (EMC) (volume ratio=1:1:1) and vinylene carbonate (VC)(1.0% by mass) as an electrolytic solution, a polyethylene microporousfilm having a thickness of 25 μm as a separator, and a copper platehaving a thickness of 250 μm as a spacer.

<Cell Performance (Initial Discharge Capacity, Initial Charge andDischarge Efficiency)>

The above-obtained cell was placed in a thermostat kept at 25° C., andan initial charge capacity was measured by carrying out charging at aconstant current of 0.45 mA/cm² up to 0 V and then further charging at aconstant voltage of 0 V until the current reached a value correspondingto 0.02 mA/cm². After the charging, 30-minute pause was taken and thendischarging was carried out. The discharging was carried out at acurrent of 0.45 mA/cm² until the voltage value reached 1.5 V, and thenan initial discharge capacity was measured. Here, the capacity wasconverted to a value per the mass of the negative electrode activematerial used. Calculation was performed by dividing the initialdischarge capacity by the initial charge capacity to obtain a value andthen multiplying the obtained value by 100, to obtain another value,which is defined as an initial charge and discharge efficiency (%). Theresult is shown in Table 1.

<Cycle Characteristics>

The above-obtained cell was placed in a thermostat kept at 25° C.,charged at a constant current of 0.45 mA/cm² up to 0 V and then furthercharged at a constant voltage of 0 V until the current reached a valuecorresponding to 0.02 mA/cm². After the charging, 30-minute pause wastaken and then discharging was carried out. The discharging was carriedout at a current of 0.45 mA/cm² until the voltage value reached 1.5 V.The charge and discharge was defined as one cycle. A cycle test whichincludes performing the one cycle 10 times was conducted, and a cyclecharacteristic calculated by the following equation was evaluated. Theresult is shown in Table 1.Cycle characteristics (10-cycle capacity retention rate)=[dischargecapacity at 10th cycle/discharge capacity at 1stcycle]×100(%)  Equation:

<Storage Characteristics at High Temperature (Retention Rate andRecovery Rate)>

The above-obtained cell was placed in a thermostat kept at 25° C.,charged at a constant current of 0.45 mA/cm² up to 0 V and then furthercharged at a constant voltage of 0 V until the current reached a valuecorresponding to 0.02 mA/cm². After the charging, 30-minute pause wastaken and then discharging was carried out. The discharging was carriedout at a current of 0.45 mA/cm² until the voltage value reached 1.5 V.

After the charging of second cycle was performed under the sameconditions as described above, the cell was placed in a thermostat keptat 70° C. in a charged state and stored for 72 hours. Thereafter, thecell was again placed in a thermostat kept at 25° C., and dischargingwas carried out at a current of 0.45 mA/cm⁻¹ until the voltage valuereached 1.5V. A ratio of a discharge capacity immediately after storageat 70° C. to an initial discharge capacity was defined as a retentionrate of a storage characteristics. The result is shown in Table 1.

Then, using a thermostat kept at 25° C., the charge/discharge test wasperformed in third cycle under the same conditions as described above. Aratio of a discharge capacity in the third cycle to the initialdischarge capacity was defined as a recovery rate of the storagecharacteristics. The results are given in Table 1.

Examples 2 to 4

Negative electrode active materials were produced and evaluated in thesame manner as in Example 1, except that the temperature of heattreatment at which the carbonization of the carbon source and thedisproportionation reaction of the silicon oxide were made to occur waschanged to 1000° C. (Example 2), 1050° C. (Example 3) and 1100° C.(Example 4), respectively. The results are shown in Table 1.

Comparative Examples 1 and 2

Negative electrode active materials were produced and evaluated in thesame manner as in Example 1, except that the temperature of heattreatment at which the carbonization of the carbon source and thedisproportionation reaction of the silicon oxide were made to occur waschanged to 900° C. (Comparative example 1) and 1200° C. (Comparativeexample 2), respectively. The results are shown in Table 2.

Example 5

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that the silicon oxide particleshaving a volume mean particle diameter (D50%) of 5 μm obtained after theprocess of pulverizing the silicon oxide particle were further subjectto an additional treatment of surface modification by NOBILTA (NOB-VC,Hosokawa Micron Co., Ltd.). The results are shown in Table 1.

Example 6

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that the silicon oxide particleshaving a volume mean particle diameter (D50%) of 5 μm obtained after theprocess of pulverizing the silicon oxide particles were further subjectto an additional treatment of surface modification by MECHANOFUSIONsystem (Lab, Hosokawa Micron Co., Ltd.). The results are shown in Table1.

Example 7

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that a fine impact mill: pin milltype (UPZ, Hosokawa Micron Co., Ltd.) was used as a pulverizingapparatus in the process of pulverizing the silicon oxide particles, andthe silicon oxide particles were pulverized so that a volume meanparticle diameter (D50%) became 5 μm. The results are shown in Table 1.

Example 8

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that a fine mill (SF type, NipponCoke & Engineering Co., Ltd.) was used as a pulverizing apparatus in theprocess of pulverizing the silicon oxide particles, and the siliconoxide particles were pulverized so that a volume mean particle diameter(D50%) became 5 μm. The results are shown in Table 1.

Example 9

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that the partial pressure ofacetylene gas was changed to 20%, and the duration of treatment thereofwas changed to 4 hours. The results are shown in Table 2.

Example 10

A negative electrode active material was produced and evaluated in thesame manner as in Example 2, except that a compressed natural gas wasused as a carbon source. The results are shown in Table 2.

Example 11

A negative electrode active material was produced and evaluated in thesame manner as in Example 10, except that the partial pressure of thecompressed natural gas was changed to 20%. The results are shown inTable 2.

Example 12

1000 g of silicon oxide particles with a volume mean particle diameter(D50%) of 5 μm obtained after the process of pulverizing silicon oxidein Example 1 and 34 g of petroleum-based pitch (75% by mass of fixedcarbon) as a carbon source of carbon were fed into a mixing device(Rocking Mixer RM-10G, AICHI ELECTRIC Co., Ltd.) and mixed for 5minutes, and then filled into an alumina heat treatment vessel. Afterfilling the heat treatment vessel, a heat treatment was carried out inan atmospheric sintering furnace under a nitrogen atmosphere at 1000° C.for 5 hours to carbonize the carbon source to obtain a heat treatedproduct. The obtained heat treated product was disintegrated by a mortarand sieved by a 300 M (300 mesh) test sieve to prepare a negativeelectrode active material. Subsequently, the same evaluation wasperformed as in Example 1. The results are shown in Table 2.

Example 13

A negative electrode active material was produced and evaluated in thesame manner as in Example 12, except that the amount of petroleum-basedpitch was changed to 67 g. The results are shown in Table 2.

Comparative Example 3

A negative electrode active material was produced and evaluated in thesame manner as in Example 9, except that the partial pressure ofacetylene gas was changed to 30%. The results are shown in Table 2.

TABLE 1 Example Example Example Example Example Example Example ExampleItem 1 2 3 4 5 6 7 8 Heat Treatment Temperature [° C.] 950 1000 10501100 1000 1000 1000 1000 XRD Intensity Ratio (P_(Si)/P_(SiO2)) [—] 1.31.6 1.9 2.5 1.7 1.6 1.7 1.6 Carbon Content [% by mass] 2.3 2.5 2.5 2.62.4 2.5 2.4 2.5 Size of Silicon Crystallite [nm] 2.9 4.0 5.7 7.9 4.1 4.03.9 4.0 R value (D/G) 0.9 1.0 0.9 0.9 0.9 1.0 1.0 0.9 Specific SurfaceArea [m²/g] N₂ 3.7 2.6 2.4 2.3 2.4 2.2 2.8 3.1 H₂O 1.4 1.1 0.78 0.660.97 0.73 1.5 1.8 H₂O Adsorption Amount [cm³/g] 3.2 2.2 2.5 1.4 2.1 2.22.9 3.5 Volume Mean Particle Diameter [μm] 5.8 5.7 5.6 5.6 5.5 5.6 5.65.7 D10% Particle Diameter [μm] 3.71 3.79 3.78 3.76 3.97 4.03 1.48 1.32D90% Particle Diameter [μm] 8.28 8.52 8.40 8.43 7.78 7.42 11.65 11.48D10%/D90% [μm] 0.448 0.445 0.450 0.446 0.510 0.543 0.127 0.115 Meanaspect ratio [—] 0.70 0.74 0.75 0.72 0.84 0.90 0.69 0.57 InitialDischarge Capacity [mAh/g] 1349 1399 1418 1442 1443 1466 1355 1332Initial Charge and Discharge Efficiency [%] 68.1 71.5 72.1 73.2 72.874.0 70.7 70.0 Storage Characteristics at High 91.1 91.9 92.2 91.3 92.695.8 91.4 90.6 Temperature/Retention Rate [%] Storage Characteristics atHigh 88.7 89.1 90.1 89.0 91.5 95.7 88.9 88.0 Temperature/Recovery Rate[%] 10-Cycle Capacity Retention Rate [%] 82.8 84.6 85.9 84.3 87.9 91.882.9 82.2

TABLE 2 Example Example Example Example Example Comparative ComparativeComparative Item 9 10 11 12 13 Example 1 Example 2 Example 3 HeatTreatment Temperature [° C.] 1000 1000 1000 1000 1000 900 1200 1000 XRDIntensity Ratio (P_(Si)/P_(SiO2)) [—] 1.6 1.6 1.7 1.6 1.7 0.9 2.9 1.6Carbon Content [% by mass] 9.7 2.3 5.9 2.5 4.9 2.4 2.5 15.3 Size ofSilicon Crystallite [nm] 4.1 5.1 4.9 4.1 4.0 1.7 16.9 4.2 R value (D/G)0.9 0.8 0.9 0.9 0.9 1.0 1.0 1.0 Specific Surface Area [m²/g] N₂ 4.2 2.12.0 2.7 3.0 4.5 2.0 10.8 H₂O 2.5 0.55 0.51 1.0 1.2 2.1 0.52 6.7 H₂OAdsorption Amount [cm³/g] 6.6 1.8 1.6 2.3 2.9 4.6 1.1 8.6 Volume MeanParticle Diameter [μm] 6.7 5.7 5.8 5.5 5.6 5.5 5.6 7.4 D10% ParticleDiameter[μm] 3.80 4.31 4.53 3.80 3.79 3.79 3.80 3.61 D90% ParticleDiameter[μm] 8.44 9.82 9.98 8.48 8.52 8.48 8.52 8.78 D10%/D90%[μm] 0.4500.439 0.454 0.448 0.445 0.447 0.446 0.411 Mean aspect ratio [—] 0.730.74 0.74 0.73 0.74 0.73 0.75 0.78 Initial Discharge Capacity [mAh/g]1377 1454 1461 1386 1389 1330 902 1191 Initial Charge and DischargeEfficiency [%] 70.5 74.0 73.9 70.1 70.5 66.8 73.5 67.9 StorageCharacteristics at High 91.3 95.1 95.6 91.2 92.0 87.2 90.1 88.2Temperature/Retention Rate [%] Storage Characteristics at High 88.8 95.695.2 88.9 89.5 83.5 87.1 86.3 Temperature/Recovery Rate [%] 10-CycleCapacity Retention Rate [%] 85.7 92.2 92.8 84.0 85.1 78.3 81.9 81.6

As shown in Tables 1 and 2, the lithium-ion secondary batteries ofExamples 1 to 13, each of which using the negative electrode activematerial having the X-ray diffractive peak intensity ratio(P_(Si)/P_(SiO2)), the H₂O specific surface area, and the amount ofadsorption of H₂O satisfying the specified conditions, exhibited initialdischarge capacities and storage characteristics at high temperature.

The negative electrode active materials of Comparative examples 1 and 2,each of which failed to satisfy the specified condition of the X-raydiffractive peak intensity ratio (P_(Si)/P_(SiO2)), were inferior toExamples in terms of the initial discharge capacity.

The negative electrode active materials of Comparative example 3, ofwhich failed to satisfy both of the H₂O specific surface area and theamount of adsorption of H₂O, were inferior to Examples in terms of bothof the initial discharge capacity and the storage characteristics athigh temperature.

All publications, patent applications, and technical standards mentionedin this specification are herein incorporated by reference to the sameextent as if each individual publication, patent application, ortechnical standard was specifically and individually indicated to beincorporated by reference.

EXPLANATION OF REFERENCE NUMERALS

-   10: Carbon-   12: Carbon granule-   20: Silicon oxide particle

The invention claimed is:
 1. A negative electrode active material for alithium ion secondary battery, the negative electrode active materialcomprising silicon oxide particles, each of which has carbon on at leasta portion of its surface, wherein: a ratio (P_(Si)/P_(SiO2)) of anintensity of an X-ray diffraction peak at 2θ of from 27° to 29°, whichis derived from Si, to an intensity of an X-ray diffraction peak at 2θof from 20° to 25°, which is derived from SiO₂, is within a range offrom 1.0 to 2.6, when CuKα radiation having a wavelength of 0.15406 nmis used as a radiation source; and a specific surface area calculatedfrom moisture adsorption at 298 K is 6.5 m²/g or less, wherein thenegative electrode active material has a ratio (D10%/D90%) of 0.1 orgreater, in which D90% is a particle diameter corresponding to 90%cumulative from a smaller particle diameter side in a cumulative volumedistribution curve obtained by a laser diffraction/scattering method,and D10% is a particle diameter corresponding to 10% cumulative from thesmaller particle diameter side in the cumulative volume distributioncurve.
 2. A negative electrode active material for a lithium ionsecondary battery, the negative electrode active material comprisingsilicon oxide particles, each of which has carbon on at least a portionof its surface, wherein: a ratio (P_(Si)/P_(SiO2)) of an intensity of anX-ray diffraction peak at 2θ of from 27° to 29°, which is derived fromSi, to an intensity of an X-ray diffraction peak at 2θ of from 20° to25°, which is derived from SiO₂, is within a range of from 1.0 to 2.6,when CuKα radiation having a wavelength of 0.15406 nm is used as aradiation source; and an amount of adsorption of moisture up to arelative pressure of 0.95 at 298 K is 8.5 cm³/g or less, wherein thenegative electrode active material has a ratio (D10%/D90%) of 0.1 orgreater, in which D90% is a particle diameter corresponding to 90%cumulative from a smaller particle diameter side in a cumulative volumedistribution curve obtained by a laser diffraction/scattering method,and D10% is a particle diameter corresponding to 10% cumulative from thesmaller particle diameter side in the cumulative volume distributioncurve.
 3. The negative electrode active material for a lithium ionsecondary battery according to claim 1, wherein an mean aspect ratiorepresented by a ratio (S/L) of a minor axis S to a major axis L iswithin a range of 0.45≤S/L≤1.
 4. The negative electrode active materialfor a lithium ion secondary battery according to claim 1, wherein acontent of the carbon is within a range from 0.1% by mass to 10.0% bymass of a total of the silicon oxide particles and the carbon.
 5. Thenegative electrode active material for a lithium ion secondary batteryaccording to claim 1, the negative electrode active material having adiffraction peak that is attributed to Si (111) in X-ray diffractionspectra, wherein a size of silicon crystallites calculated from thediffraction peak is from 1.0 nm to 15.0 nm.
 6. The negative electrodeactive material for a lithium ion secondary battery according to claim1, wherein a volume mean particle diameter is from 0.1 μm to 20 μm. 7.The negative electrode active material for a lithium ion secondarybattery according to claim 1, wherein a specific surface area calculatedfrom nitrogen adsorption at 77 K is from 0.1 m²/g to 10 m²/g.
 8. Thenegative electrode active material for a lithium ion secondary batteryaccording to claim 1, further comprising a carbon-based negativeelectrode active material.
 9. A negative electrode for a lithium ionsecondary battery, the negative electrode comprising: a currentcollector; and a negative electrode material layer that is provided onor above the current collector and that comprises the negative electrodeactive material for a lithium ion secondary battery according toclaim
 1. 10. A lithium ion secondary battery, comprising: a positiveelectrode; the negative electrode for a lithium ion secondary batteryaccording to claim 9; and an electrolyte.
 11. The negative electrodeactive material for a lithium ion secondary battery according to claim2, wherein an mean aspect ratio represented by a ratio (S/L) of a minoraxis S to a major axis L is within a range of 0.45≤S/L≤1.
 12. Thenegative electrode active material for a lithium ion secondary batteryaccording to claim 2, wherein a content of the carbon is within a rangefrom 0.1% by mass to 10.0% by mass of a total of the silicon oxideparticles and the carbon.
 13. The negative electrode active material fora lithium ion secondary battery according to claim 2, the negativeelectrode active material having a diffraction peak that is attributedto Si (111) in X-ray diffraction spectra, wherein a size of siliconcrystallites calculated from the diffraction peak is from 1.0 nm to 15.0nm.
 14. The negative electrode active material for a lithium ionsecondary battery according to claim 2, wherein a volume mean particlediameter is from 0.1 μm to 20 μm.
 15. The negative electrode activematerial for a lithium ion secondary battery according to claim 2,wherein a specific surface area calculated from nitrogen adsorption at77 K is from 0.1 m²/g to 10 m²/g.
 16. The negative electrode activematerial for a lithium ion secondary battery according to claim 2,further comprising a carbon-based negative electrode active material.17. A negative electrode for a lithium ion secondary battery, thenegative electrode comprising: a current collector; and a negativeelectrode material layer that is provided on or above the currentcollector and that comprises the negative electrode active material fora lithium ion secondary battery according to claim
 2. 18. A lithium ionsecondary battery, comprising: a positive electrode; the negativeelectrode for a lithium ion secondary battery according to claim 17; andan electrolyte.
 19. The negative electrode active material for a lithiumion secondary battery according to claim 2, wherein the negativeelectrode active material has a ratio (D10%/D90%) of 0.3 or greater. 20.The negative electrode active material for a lithium ion secondarybattery according to claim 1, wherein the negative electrode activematerial has a ratio (D10%/D90%) of 0.3 or greater.